A novel approach for the surface modification of hydroxyapatite (HAp) nanocrystals is described by grafting polymerization of vinyl phosphonic acid (VPA) using a redox initiating system in an aqueous media. Fourier transform infrared (FT-IR) and XRD analyses confirmed the modification reaction on HAp surfaces. Inductively coupled plasma mass spectroscopy (ICP MS) showed that the Ca/P molar ratio decreased from 1.67 to 1.36 with increasing the feed VPA amount. Zeta potentials of unmodified HAp and modified HAp in phosphate-buffered saline (PBS) solutions (pH 7.4, ionic strength = 10 mM) were negative and decreased with increasing the amount of grafted PVPA. Transmission electron microscopy (TEM) measurements and time-dependent phase monitoring indicated that the colloidal stability of modified HAp over unmodified HAp in water dramatically increased and tended to exist as single nanocrystals without aggregation. (c) 2006 Elsevier Inc. All rights reserved.