Ti45--xZr35--xNi17+2rCU3 (x=0, 2, 4, 6 and 8) icosahedral quasicrystalline phase (I-phase) alloy powders are synthesized by mechanical alloying and subsequent annealing techniques, and the crystallographic and electrochemical characteristics are investigated. The alloy powders are I-phase, and the quasi-lattice constant decreases with increasing x value. The maximum discharge capacity of the I-phase alloy electrodes first increases and then decreases with increasing x value, and the Ti39Zr26Ni29Cu3 I-phase electrode exhibits the highest discharge capacity of 274 mAh g(--1). The high-rate dischargeability at the discharge current density of 240mA g(--1) increases from 55.31 % (x= 0) to 74.24% (x= 8). Cycling stability also increases with increasing x value. The improvement in electrochemical characteristics may be ascribed to the added nickel, which not only improves the electrochemical activity, but also makes the alloy more resistant to oxidation. (C) 2006 Elsevier B.V. All rights reserved.