This paper shows and discusses the results obtained after an experimental session devoted to characterization of the behavior of a single proton exchange membrane fuel cell (PEMFC) with variation of the values of six operation variables: cell temperature; anode flow temperature in saturation and dry conditions; cathode flow temperature in saturation and dry conditions; and reactants pressure. The fuel cell employed for the experiments is a single PEMFC with a 25 cm(2) Nafion((R)) 115 membrane. As expected, a higher cell temperature increases the membrane conductivity and the exchange current density with an improvement of the cell behaviour. An increase in the reactant saturation temperature also leads to a better performance, especially in the case of low and medium loads. Conversely, in the case of a low cell temperature, it is better to reduce the water inlet mass flow at high loads to avoid electrode flooding. With an increase of the reactant operating pressure, the maximum of the power curve shifts to higher current densities, and this could be linked to the corresponding shift of the limiting current density. A combined effect of humidification and operating pressure was observed: the increase of operating pressure did not offer a significant improvement when the reactants were dry, while leading to improvements when a partial humidification (only at the anode) was adopted. The best improvements due to a pressure increase were observed when both anode and cathode are humidified. Finally, some tests of other authors at the same operation conditions have been considered, and a comparison has been done. (c) 2006 Elsevier Ltd. All rights reserved.