Solid State Ionics, Vol.177, No.19-25, 1819-1822, 2006
Synthesis and electrical conductivity of Sr- and Mn-substituted LaAlO3 as a possible SOFC anode material
Single phase (La,Sr)(Al,Mn)O-3 perovskites were synthesized and their electrical conductivity was studied as a function of temperature and oxygen partial pressure. The electrical conductivity was found to increase with Mn content, temperature and oxygen partial pressure, thus (La, Sr) (Al, Mn)O-3 may be regarded as a diluted system of (La,Sr)MnO3. The highest electrical conductivity at 810 degrees C in air and humidified Ar/4% H-2 was observed for (La0.8Sr0.2)(0.94)Al0.5Mn0.5O3 and reached 12 and 2.7 S/cm, respectively. (c) 2006 Elsevier B.V. All rights reserved.