A novel fabrication process for advanced composite components-the Quicktep (TM) process was described. 2/2 twill weave MTM56/CF0300 carbon epoxy composite laminates were manufactured by the Quickstep and the autoclave processes. The response of these laminates to drop-weight low velocity impact at energy levels ranging from 5 to 30 J was investigated. It was found that the laminates fabricated by the Quickstep had better impact damage tolerance than those fabricated by the autoclave. Optical microscopy revealed extensive matrix fracture in the center of the backside of the autoclave laminates indicating the more brittle property of the epoxy matrix cured by the autoclave process. Interfacial shear strength (IFSS) for two composite systems were measured by micro-debond experiments. The MTM56/CF0300 material cured by the Quickstep showed stronger fibre matrix adhesion. Since the thickness and density of the impact targets produced by two processes were different, finite element analysis (FEA) was performed to study the effect of these factors on the impact response. The simulation results showed that the difference in thickness and density affects the stress distribution under impact loading. Higher thickness and lower density caused by processing lead to less endurance to drop weight impact loading. Therefore the better performance of Quickstep laminates under impact loading was not due to the thickness and density change, but resulted from stronger mechanical properties.