We examine the morphological structures of asymmetric poly(ethylene oxide)-b-poly(1,1'-dihydroperflurooctyl methacrylate) (PEO-b-PFOMA) thin films upon annealing in a compressible fluid, supercritical CO2 (Sc-CO2). The strong affinity between PFOMA and CO2 is found to induce phase segregation when annealing PEO-b-PFOMA films at the same temperature as compared with vacuum. In vacuum, PEO-b-PFOMA films remain disordered from 80 to 180 degrees C, whereas, in Sc-CO2 at 13.9 MPa, an upper order-disorder transition (UODT) between 116 and 145 degrees C is found. In Sc-CO2, the observed ordered structure is layers of PEO spheres embedded in the matrix of PFOMA, followed by a brush layer, in which PEO wets the substrate. The swelling isotherms of PFOMA and PEO in CO2 are correlated with the Sanchez-Lacombe equation of state (SLEOS) to estimate the interaction parameters, chi(PFOMA-CO2) and chi(PEO-CO2). The phase segregation (order) induced by CO2 relative to vacuum at a given temperature is explained in terms of two factors: (1) copolymer volume fraction upon dilution with CO2, phi, and (2) the relative interaction parameter, Delta chi = chi(PEO-CO2) -chi(PFOMA-CO2). The latter factor favors order and is dominant at low temperatures over the phi factor, which always favors disorder. At high temperatures (above the T-ODT), the preferential swelling of PFOMA by CO2 is less pronounced (Delta chi decreases), and the copolymer is disordered.