Alkylketene dimer (AKD), a kind of wax, has been known to form fractal surfaces spontaneously and show super water-repellency. Such formation of water-repellent and fractal surfaces was also found in this work for triglycerides. Since the crystal phase transitions of these waxes were well studied, we studied the formation of their fractal surfaces through contact angle measurements, differential scanning calorimetry (DSC), and X-ray diffraction (XRD). From time-dependent contact angle measurements, it was found that the formation of super water-repellent surfaces with fractal structures occurred spontaneously also on the triglyceride surfaces at different temperatures. The freshly solidified triglyceride surfaces were almost transparent, and their initial contact angles of water were close to 110 degrees. The surfaces then became rough and clouded after being incubated for a certain time at a specified temperature. The super water-repellent surfaces were quite rough and showed fractal structures with the dimension of ca. 2.2 calculated from the scanning electron microscopic (SEM) images by the box-counting method. The phase transformation from a metastable state to a stable cystalline one after the solidification from the melt of triglycerides was clearly observed by DSC and XRD measurements. The fractal crystalline structures and the super water-repellency resulted from this phase transformation and the crystal growth. Ensuring the initial sample solidified into the metastable state and curing the surface at an appropriate temperature are key factors for the successful preparation of fractal triglyceride surfaces by the solidification method.