Intense Tm3+ blue upconversion emission has been observed in Tm3+-Yb3+ codoped oxyfluoride tellurite glass under excitation with a diode laser at 976 nm. Three emission bands centered at 475, 650 and 796 nm corresponding to the transitions (1)G(4) -> H-3(6), (1)G(4) -> H-3(4) and F-3(4) -> H-3(6), respectively, simultaneously occur. The dependence of upconversion intensities on Tm3+ ions concentration and excitation power are investigated. For fixed Yb2O3 concentrations of 5.0 mol%, the maximum upconversion intensity was obtained with Tm2O3 concentration of about 0.1 mol%. The blue upconversion luminescence lifetimes of the Tm3+ transitions (1)G(4) -> H-3(6) are measured. The results are evaluated by the possible upconversion mechanisms.