2,2-Dimethoxy-propane (DMP) was studied as an additive in 1 mol dm(-3) LiPF6 ethylene carbonate and diethyl carbonate (1: 1, w/w) for lithiumion battery, which was characterized by cyclic voltammetry and half cell tests. Cyclic voltammetry and half cell data show that the use of DMP as an additive to the organic solutions at very low level (ca. 0.005 wt%) offers the advantage of forming fully developed passive films on the graphite anode surface. The electrochemical performance of the additive-containing electrolytes in combination with LiCoO2 cathode and graphitic anode was also tested in commercial cells 103448. The results reveal that the cyclic life test and storage performance at high temperature (ca. 60 degrees C) in electrolyte with DMP additive was better than that in an electrolyte without additive. Therefore, DMP can be considered as a desirable additive in electrolyte for lithium-ion batteries operating at high temperature, ca. 60 degrees C. (c) 2006 Elsevier B.V. All rights reserved.