Recovery and delivery rate of hydrogen from ZrCoH1.6 at different temperatures were measured. 19.7L of hydrogen at ~1bar was absorbed into a ZrCo of 160g at room temperature. 83%, 98%, 100% of hydrogen was absorbed in 10, 30, 60 minutes, respectively. Until 30 minutes of delivery, average delivery rate was measured to be 0.28Pam3/s at 250-350℃, 0.29Pam3/s at 275-350℃ and 0.45Pam3/s at 300-350℃. From this experiment, preheating temperature was found to be higher than 300℃. During repetition of delivery for 1350 sec and preheating for 450 sec at 350℃, average delivery rate was measured to be 0.32Pam3/s at the first delivery, 0.26Pam3/s at the second delivery and 0.22Pam3/s at the third delivery, respectively.