Journal of Industrial and Engineering Chemistry, Vol.13, No.3, 387-394, May, 2007
Export Citation
Effect of Polymer Cement Modifiers on Mechanical and Physica Properties of Polymer-Modified Mortar Using Recycled Waste Concrete Fine Aggregate
Eui-Hwan Hwang†, Young Soo Ko, and Jong-Ki Jeon
  • Department of Chemical Engineering, Kongju National University, Chungnam-do 330-717, Korea
E-mail:
Various polymer-modified mortars using recycled waste concrete fine aggregate were prepared and investigated for the purpose of measuring their feasibility of recycling. Styrene-butadiene rubber (SBR) latex and polyacrylic ester (PAE) emulsion were used and compared as polymer cement modifiers. The replacement ratio of waste concrete fine aggregate (WCFA) was also changed to investigate its effect on the physical properties. The addition of a polymer cement modifier into the mortar reduced the water-cement ratio significantly; PAE was more effective at reducing the water-cement ratio than was SBR. There was slight difference in water absorption between the SBR- and PAE-modified mortars, and it decreased drastically at a 20 % content of polymer cement modifier for both SBR and PAE. The compressive strengths decreased after the addition of the polymer cement modifiers; the PAE emulsion-modified mortar showed higher flexural strength than did the SBR latex-modified one. After the hot water resistance test, the compressive strength of the 20 % polymer cement modifier had a slightly lower value than did that at 10 % for both SBR and PAE; the rate of decrease in flexural strength of the specimen was more rapid in case of the PAE-modified mortar relative to that of the SBR-modification.
Keywords:ploymer-modified mortar;polymer cement modifier;polymer-cement ratio;recycling;waste concrete
  1. Kim JM, Lee SH, Yun HD, J. Concr. Inst., 15, 14 (2003)
  2. Kim MH, Kang SP, J. Concr. Inst., 15, 2 (2003)
  3. Tomosawa F, Noguchi T, in Proc. Integrated Design and Environmental Issues in Concrete Technology, K. Sakai Ed., pp. 263-272, London, England (1996)
  4. Song HW, Byun KJ, Ha JH, J. Korea Concr. Inst., 12, 3 (2000)
  5. Hwang EH, Choi JJ, Hwang TS, J. Korean Ind. Eng. Chem., 16(3), 317 (2005)
  6. Kim MH, J. Korea Concr. Inst., 10, 52 (1998)
  7. Evbuomwan NFP, in Proc. 6th Intern. Symp. Polymers in Concrete, H. Yiun-Yuan, W. Keru and C. Zhiyuan Eds., pp. 52-59, Shanghai, China (1990)
  8. Viswanath P, Thachil ET, in Proc. 5th Asian Symp. Polymers in Concrete, N. Laksmanan, C. V. Vaidyanathan, Y. Ohama, and M. Neelamegam Eds., pp.125-132, Chennai, India (2006)
  9. Andrea D, Jochen S, in Proc. 9th Intern. Symp. Polymers in Concrete, F. Sandrolini Ed., pp.611-631, Bologna, Italy (1998)
  10. Hwang EH, Kil DS, Hwang TS, J. Korean Ind. Eng. Chem., 11(7), 792 (2000)
  11. Hwang EH, Hwang TS, Kil DS, J. Korean Ind. Eng. Chem., 10(7), 1066 (1999)
  12. Hwang EH, Kil DS, Oh IS, J. Korean Ind. Eng. Chem., 8(6), 979 (1997)
  13. Lee JM, Shim SE, Choe S, J. Ind. Eng. Chem., 12(4), 648 (2006)
  14. Yeon KS, in Proc. 5th Asian Symp. Polymers in Concrete, N. Laksmanan, C. V. Vaidyanathan, Y. Ohama and M. Neelamegam Eds., pp. 13-28, Chennai, India (2006)
  15. Ohama Y, Shiroishida K, SP-89, American Concrete Institute, pp. 313-322 (1985)
  16. Ohama Y, in Proc. 9th Intern. Symp. Polymers in Concrete, F. Sandrolini Ed., pp. 1-19, Bologna, Italy (1998)
  17. Fowler DW, Depuy GW, in Proc. 8th Intern. Symp. Polymers in Concrete, D. Van Gemert and K.U. Leuven Eds., pp. 67-73, Oostende, Belgium (1995)
  18. Swamy RN, in Proc. 8th Intern. Symp. Polymers in Concrete, D. Van Gemert and K. U. Leuven Eds., pp. 21-26, Oostende, Belgium (1995)
  19. Hwang EH, Hwang TS, Ohama Y, J. Korean Ind. Eng. Chem., 5(5), 786 (1994)
  20. Hwang EH, Hwang TS, Kamada EiJi, J. Korean Ceramic Soc., 31, 949 (1994)
  21. Ohama Y, Adv. Cem. Based Mater., 5, 31 (1997)
  22. Chandra S, in Proc. 9th Intern. Symp. Polymers in Concrete, F. Sandrolini Ed., pp. 733-738, Bologna, Italy (1998)
  23. Ohama Y, Demura K, Kim WK, in Proc. 8th Intern. Symp. Polymers in Concrete, D. Van Gemert and K. U. Leuven Eds., pp. 251-256, Oostende, Belgium (1995)
  24. Hwang EH, Hasegawa T, Hama Y, Kamada E, Ohama Y, in Proc. 1st Asian Symp. Polymers in Concrete, K. S. Yeon and J. D. Choi Eds., pp. 53-80, Chuncheon, Korea (1994)
  25. Swamy RN, Nagao H, in Proc. 8th Intern. Symp. Polymers in Concrete, D. Van Gemert and K.U. Leuven Eds., pp. 257-262, Oostende, Belgium (1995)
  26. Ohama Y, Miyake M, in Proc. 8th Intern. Symp. Polymers in Concrete, D. Van Gemert and K.U. Leuven Eds., pp. 331-336, Oostende, Belgium (1995)
  27. Jo YK, Ohama Y, Demura K, in Proc. 1st Asian Symp. Polymers in Concrete, K. S. Yeon and J. D. Choi Eds., pp. 231-240, Chuncheon, Korea (1994)
  28. Hwang EH, Rho JS, Hwang TS, Lee BK, J. Korean Soc. Waste Manage., 19, 292 (2002)
  29. Hwang EH, Kil DS, Rho JS, Hwang TS, Lee BK, J. Korean Soc. Waste Manage., 19, 275 (2002)
  30. Hwang EH, Han CG, Choi JJ, Lee BK, J. Korean Concr. Inst., 14, 190 (2002)
  31. Ohama Y, Concrete Admixtures Handbook, p. 337, Noyes Publication, New Jersey (1984)
  32. Hashimoto H, Ohama Y, The International of the College of Engineering of Nihon University, Series A, 19, p. 113 (1987)
  33. Sakai E, Sugita J, Cem. Concr. Res., 25, 127 (1995)
  34. Evbuomwan NFO, in Proc. 6th Intern. Symp. Polymers in Concrete, H. Yiun-Yuan, W. Keru, and C. Zhiyuan Eds., p. 52, Shanghai, China (1990)
  35. Semerad E, Kremnitzer P, Lacom W, Holub F, Sattler P, in Proc. 5th Intern. Symp. Polymers in Concrete, B. W. Staynes Ed., p. 223, Brighton, England (1987)