Clean Technology, Vol.13, No.2, 127-133, June, 2007
Export Citation
세라이트필름과 폴리에틸렌 필름의 방청효과 및 기계적 물성 비교
Comparison of Anti-rust Effect and Mechanical Properties of Celite Film and Polyethylene Film
정용찬1, †, 서수열1, 전병철2, 3
  • 1수원대학교 화학과, 445-743 경기도 화성시 봉담읍 와우리 산2-2
  • 2수원대학교 신소재공학과, 445-743 경기도 화성시 봉담읍 와우리 산2-2
  • 3서울대학교 지능형 텍스타일 연구센터, 151-744 서울시 관악구 신림동 산56-1
Yong-Chan Chung1, †, Soo Yul Suh1, and Byoung Chul Chun2, 3
  • 1Dept. of Chemistry, The University of Suwon, San 2-2, Wawoo-ri, Bongdam-eup, Hwasung City, Kyonggi-do 445-743, Korea
  • 2†Dept. of Polymer Engineering, The University of Suwon, San 2-2, Wawoo-ri, Bongdam-eup, Hwasung City, Kyonggi-do 445-743, Korea
  • 3Intelligent Textile Research Center, Seoul National University, San 56-1, Shilim-dong, Kwanak-gu, Seoul 151-744, Korea
E-mail:
초록
세라이트는 내부 공동이 매우 넓어서 그 내부에 다양한 분자성 물질을 저장할 수 있으며, 세라이트 분말은 PE 필름 내부에 잘 분산될 수 있어서 세라이트를 함유한 PE 필름을 제조할 수 있었다. 표면을 계면활성제로 처리하여 극성을 낮춘 세라이트를 함유한 PE 필름 그리고 표면 처리하지 않은 세라이트를 이용한 PE 필름 등 2가지 필름을 제조하였다. 제조된 필름내부의 세라이트 내부 공동에는 방청물질인 dicyclohexylamine, dicyclohexylamine nitrite 또는 diisopropylamine 등이 스며들게 하여, 포함된 방청분자들이 서서히 외부로 방출되게 함으로서 필름 백 내부에 포장된 철물에 대한 방청효과를 지속적으로 발휘하도록 하였다. 여러가지 밀봉필름 백 내부의 방청물질 농도 변화를 gas chromatography를 이용하여 한 달간 각 필름 백의 방청물질 발산 지속기간을 비교하였고, 실제로 실험실에서 사용되는 철물을 대상으로 6개월에 걸쳐 방청실험을 진행하였다. 실험 결과 세라이트 필름은 일반 PE 필름에 비해 방청효과가 뛰어나며, 방청물질 발산 지속기간이 우수하였다.
Celite with enormous pore space inside can hold small molecules and can be well blended with polyethylene (PE) to make a Celite-PE film. Two types of Celite-PE film were prepared, one with Celite surface-treated with surfactant to reduce the hydrophilicity and another with plain Celite. The anti-rust chemical such as dicyclohexylamine, dicyclohexylamine nitrite, or diisopropylamine was allowed to permeate into celite pore in the film, and slowly evaporated to protect the packaged steel material from the rust for a long period of time. The chemical concentration in the different packaging film bags was analyzed by a gas chromatography for a month, and the anti-rust effect on iron labware was compared for a six month period. The Celite film was superior to PE film in anti-rust effect and the long-term anti-rust chemical evaporation.
Keywords:방청효과;세라이트;내부 공동;표면처리;서방성
  1. Hodge P, Sherrington DC, Polymer-supported Reactions in Organic Synthesis, Wiley, New York (1980)
  2. Polshettiwar V, Kaushik MP, Catal. Commun., 5(9), 515 (2004)
  3. Shah STA, Khan KM, Fecker M, Voelter W, Tetrahedron Lett., 44, 6789 (2003)
  4. Basso A, Martin L, Ebert C, Gardossi L, Linda P, J. Mol. Catal. B-Enzym., 8(4), 245 (2000)
  5. Khare SK, Nakajima M, Food Chem., 68(2), 153 (2000)
  6. Basso A, Ducret A, Gardossi L, Lortie R, Tetrahedron Lett., 43(11), 2005 (2002)
  7. Chong MH, Chun BC, Chung YC, Cho BG, J. Appl. Polym. Sci., 99(4), 1583 (2006)
  8. Chun BC, Lee SJ, Chung MH, Park JH, Park HW, Chung YC, Kweon OC, Korean J. Food Pres., 11(1), 478 (2004)
  9. Hwang SW, Chung YC, Chun BC, Lee SJ, Polym.(Korea), 28(5), 374 (2004)
  10. Chun BC, Chung YC, Park HW, Han KH, Fiber. Polym., 6, 200 (2005)
  11. Lee BS, Chun BC, Chung YC, Fiber. Polym., 5(2), 145 (2004)
  12. Hwang SW, Chung YC, Chun BC, Lee SJ, Polym.(Korea), 28(5), 374 (2004)
  13. Zobel MGR, Polym. Test, 3(2), 133 (1982)