Direct synthesis of fct-structured FePt nanoparticles was successfully achieved by using poly(N-vinyl-2-pyrrolidone) as a protective reagent at lower temperature than the case using low molecular weight ligands as a protective reagent. Experimental data suggest that a transformation of FePt nanoparticles from face-centered cubic to face-centered tetragonal (fct) structure takes place at reaction temperature of 261 degrees C. The results of XRD and the magnetic properties exhibit that the FePt nanoparticles synthesized at 261 degrees C have partially ordered fct-structure and a ferromagnetic behavior at room temperature. (c) 2007 Elsevier Inc. All rights reserved.