Fibrocartilage, a tissue with macromaterial properties between dense fibrous tissue and hyaline cartilage, is not well understood in its ultrastructure and regional viscoelastic properties. Here nanoindentation with atomic force microscopy was performed on fresh fibrocartilage samples of rabbit jaw joint condyles. Each sample was divided into anteromedial, anterolateral, posteromedial, and posterolateral regions for probing and topographic imaging in 2 x 2 mum and 10 x 10 mum scan sizes. Young's moduli differed significantly among these regions in a descending gradient from the anteromedial (2.34 +/-0.26 MPa) to the posterolateral (0.95 +/- 0.06 MPa). The Poisson ratio, defined as lateral strain over axial strain, had the same gradient distribution: highest for the anteromedial region (0.46 +/- 0.05) and lowest for the posterolateral region (0.31 +/- 0.05). The same four regions showed a descending gradient of surface roughness: highest for the anteromedial (321.6 +/- 13.8 nm) and lowest for the posterolateral (155.6 +/- 12.6 nm). Thus, the regional ultrastructural and viscoelastic properties of fibrocartilage appear to be coregulated. Based on these region-specific gradient distributions, fibrocartilage is constructed to withstand tissue-borne shear stresses, which likely propagate across its different regions. A model of shear gradient and concentric gradient is proposed to describe the region-specific capacity of fibrocartilage to sustain shear stresses in tendons, ligaments, joints, and the healing bone across species.