The properties of solid oxide fuel cell (SOFC) anode functional layers prepared by impregnation of ceria and catalytic metals into porous yttria-stabilized zirconia (YSZ) have been examined for operation at 973 K. By varying the thickness of the functional layer, the conductivity of the ceria-YSZ composite was determined to be only 0.015-0.02 S/cm. The initial performance of anodes made with ceria loadings of 40 or 60 wt % were similar but the anodes with lower loadings lost conductivity above 1073 K due to sintering of the ceria. The addition of dopant levels of catalytic metals was found to be critical. The addition of 1 wt % Pd or Ni decreased the anode impedances in humidified H-2 dramatically, while the improvement with 5 wt % Cu was significant but more modest. Pd doping also decreased the anode impedance in dry CH4 much more than did Cu doping; however, addition of either Pd or Cu led to similar improvements for operation in n-butane. Based on these results, suggestions are made for ways to improve SOFC anode functional layers. (C) 2007 The Electrochemical Society.