Temperature-controlled-growth of silver nanoclusters in soda glass matrix is investigated by low-frequency Raman scattering spectroscopy. Growth of the nanoclusters is ascribed to the diffusion-controlled precipitation of silver atoms due to annealing the silver-exchanged soda glass samples. For the first time, Rutherford backscattering measurements performed in this system to find out activation energy for the diffusion of silver ions in the glass matrix. Activation energy for the diffusion of silver ions in the glass matrix estimated from different experimental results is found to be consistent. (C) 2004 Elsevier B.V. All rights reserved.