LiFe0.97Co0.03O1.95Cl0.05 has been synthesized at 150degreesC using the solid-state, method. A Li/LiFeO2, cell as reported previously exhibited a large capacity decline until 15 cycles. To obtain a good cycleability of LiFeO2, Co and Cl ions substituted some Fe and O atoms of the LiFeO2 structure. LiFe0.97Co0.03O1.95Cl0.05 showed small lattice parameters compared with those of LiFeO2. This material showed a good cycleability with fairly a high discharge capacity of over 134 mAh/g at high current density.