Ceramics containing alpha-SiAlON with improved high-temperature properties such as thermal stability and creep and oxidation resistance were synthesized. The influence of starting composition on the amount of residual grain-boundary phase has been explored. Results have been interpreted in terms of compatibility phase relationships in the Si3N4-AlN-Al2O3-Re2O3 system and transient evolutions.