Compositional influences on the spectroscopic properties of Yb3+ and the structural variations with the introduction of YbF3 were studied in fluorophosphate glasses. Emission cross-section (sigma(emi)) and gain coefficient (sigma(emi) x tau(f)) were calculated which exhibit maximum at RF2 = 33 mol%. YbF3 has an important effect on the glass forming ability of fluorophosphate glasses when RF2 is over 36 mol%. The study of Raman spectra showed big differences on the glass structure between non-Yb3+ and Yb3+ -doped glasses. The main building units in Yb3+-doped samples are metaphosphate groups, pyrophosphate groups (P-2(O,F)(7), PO3F), Al[F-6] +Al[O,F](6) and F3Al-O-AlF3 while those of the non-Yb3+-doped glasses are monophosphate group P(O,F)(4), little pyrophosphate group, Al[F-4] + Al[F-6] + Al[O,F](4) + Al[O,F](6) and F3Al-O-AlF3, which means Yb3+ ions contribute to a better glass polymerization and network uniformity. (C) 2004 Elsevier B.V. All rights reserved.