One-step synthesis of Pt-loaded carbon nanoparticles including single-wall carbon nanohorns (SWNHs) by arc plasma in liquid nitrogen was demonstrated using Pt-contained graphite anode. The size distribution of Pt particles can be controlled by adjusting the concentration of Pt in the graphite anode. In the observation by transmission electron microscope, the diameter of less than 5 nm of Pt particles were observed as approximately 90% among the Pt particles when Pt was contained in the anode at 1.3 at.%. When Pt concentration in the anode was decreased to 0.4 at.%, the percentage of Pt particles whose diameter is less than 5 nm decreased to approximately 60%. It was verified that the as-grown Pt-loaded products produced by this method can be useful for the power generation by polymer electrolyte fuel cell. (c) 2005 Elsevier B.V. All rights reserved.