Nanocrystalline Ni0.5Zn0.5Fe2O4 with average particle size of similar to 9 nm has been synthesized by an autocombustion method and characterized by powder XRD, TEM and room temperature magnetic measurements. High room temperature magnetization comparable to that of the bulk material is obtained for the nanosized powders annealed at 800 degrees C, with a maximum particle size of similar to 54 nm. The results show that optimum properties can be achieved for NiZn ferrite powders synthesized by the present autocombustion method and processed at relatively lower temperatures. (c) 2005 Elsevier B.V. All rights reserved.