We have fabricated self-organized InAs/GaAs quantum dots (QDs) capped by 1 nm In0.2Al0.8As and 5 nm In0.2Ga0.8As strain-reducing layer (SRL). The luminescence emission at a long wavelength of 1.33 mum with narrower half width is realized. A wider energy separation between the ground and first excited radiative transitions of up to 102meV was observed at room temperature. Furthermore, the comparative study proves that luminescence properties of InAs/GaAs QDs overgrown with combined InAlAs and InGaAs SRLs are much better than that of one capped with InGaAs or InAlAs SRL. (C) 2002 Elsevier Science B.V. All rights reserved.