Epitaxial lateral overgrown (ELO) cubic GaN (c-GaN) on SiO2 patterned GaN/GaAs(0 0 1) substrates by metalorganic vapor phase epitaxy was investigated using transmission electron microscopy and X-ray diffraction (XRD) measurements. The density of stacking faults (SFs) in ELO c-GaN was similar to6 x 10(8) cm(-2), while that in underlying GaN template was similar to5 x 10(9) cm(-2). XRD measurements showed that the full-width at half-maximum of c-GaN (0 0 2) rocking curve decreased from 33 to 17.8 arcmin, indicating the improved crystalline quality of ELO c-GaN. The mechanism of SF reduction in ELO c-GaN was also discussed. (C) 2002 Elsevier Science B.V. All rights reserved.