The dispersion polymerization of MMA in supercritical CO2 was successfully carried out utilizing the first non-fluorous random copolymers composed of 3-tris(trimethoxysilyl)propyl methacrylate and 2-dimethylami-noethyl methacrylate, poly(SiMA-co-DMAEMA) as a stabilizer. The resulting high yield (> 93%) of micron-sized PMMA was formed in the presence of 5% (w/w to MMA) of copolymeric stabilizers. While the PSiMA and PDMAEMA homopolymer produced nondescript solid and irregular shape aggregate, respectively, the random copolymer of 71% SiMA-content resulted in spherical and uniform powder.