Polymers with eugenol moieties covalently bonded to the macromolecular chains were synthesized for potential application in orthopedic and dental cements. First, eugenol was functionalized with polymerizable groups. The synthetic methods employed afforded two different methacrylic derivatives, where the acrylic and eugenol moieties were either directly bonded, eugenyl methacrylate (EgMA), or separated through an oxyethylene group, ethoxyeugenyl methacrylate (EEgMA). A typical Fisher esterification reaction was used for the synthesis of EgMA and EEgMA, affording the desired monomers in 80% yields. Polymerization of each of the novel monomers, at low conversion, provided soluble polymers consisting of hydrocarbon macromolecules with pendant eugenol moieties. At high conversions only cross-linked polymers were obtained, attributed to participation of the allylic double bonds in the polymerization reaction. In addition, copolymers of each eugenol derivative with ethyl methacrylate (EMA) were prepared at low conversion, with the copolymerization reaction studied by assuming the terminal model and the reactivity ratios determined according to linear and nonlinear methods. The values obtained were r(EgMA) = 1.48, r(EMA) = 0.55 and r(EEgMA) = 1.22, r(EMA) = 0.42. High molecular weight polymers and copolymers were obtained at low conversion. Analysis of thermal properties revealed a T-g of 95 degrees C for PEgMA and of 20 degrees C for PEEgMA and an increase in the thermal stability for the eugenol derivatives polymers and copolymers with respect to that of PEMA. Water sorption of the copolymers was found to decrease with the eugenol derivative content. Both monomers EgMA and EEgMA showed antibacterial activity against Streptococcus mutans, producing inhibition halos of 7 and 21 mm, respectively. Finally, cell culture studies revealed that the copolymers did not leach any toxic eluants and showed good cellular proliferation with respect to PEMA. This study thus indicates that the eugenyl methacrylate derivatives are potentially good candidates for dental and orthopedic cements.