We report a study of the effects of polymer optoelectronic properties on the performance of photovoltaic devices consisting of nanocrystalline TiO2 and a conjugated polymer. Three different poly(2-methoxy-5-(2'-ethylhexoxy)-1,4-phenylenevinylene) (MEH-PPV)-based polymers and a fluorene-bithiophene copolymer are compared. We use photoluminescence quenching, time-of-flight mobility measurements, and optical spectroscopy to characterize the exciton-transport, charge-tran sport, and light-harvesting properties, respectively, of the polymers, and correlate these material properties with photovoltaic-device performance. We find that photocurrent is primarily limited by the photogeneration rate and by the quality of the interfaces, rather than by hole transport in the polymer. We have also studied the photovoltaic performance of these TiO2/polymer devices as a function of the fabrication route and device design. Including a dip-coating step before spin-coating the polymer leads to excellent polymer penetration into highly structured TiO2 networks, as was confirmed through transient optical measurements of the photoinduced charge-transfer yield and recombination kinetics. Device performance is further improved for all material combinations studied, by introducing a layer of poly(ethylene dioxythiophene) (PEDOT) doped with poly(styrene sulfonic acid) (PSS) under the top contact. Optimized devices incorporating the additional dip-coated and PEDOTYSS layers produced a short-circuit current density of about 1. mA cm(-2), a fill factor of 0.50, and an open-circuit voltage of 0.86 V under simulated AM 1.5 illumination (100 mW cm(-2), 1 sun). The corresponding power conversion efficiency under 1 sun was >= 0.4 %.