The results of field emission (FE) studies are reported for three different forms of carbon: smooth amorphous carbon (a-C) films with both low and high sp(3) content prepared by pulsed-laser deposition (PLD), nanostructured carbon prepared by hot-filament chemical-vapor deposition (HFCVD), and vertically aligned carbon nanofibers (VACNFs). The Studies reveal that smooth PLD carbon films are poor field emitters regardless of their sp(3) content. Conditioning of the films, which resulted in films' modification, was required to draw FE current and the emission turn-on fields were relatively high. In contrast, HFCVD carbon films exhibit very good FE properties, including low-emission turn-on fields, relatively high emission site density, and excellent durability. Finally, VACNFs also were found to possess quite promising FE properties that compete with those of HFCVD films. We believe that the latter two forms of carbon are among the most promising candidates for use as cold cathodes in commercial devices.