Implantation of Co or Mn into single-crystal BaTiO3(K), SrTiO3 or KTaO3(Ca), followed by annealing at 700 degreesC, produced ferromagnetic behavior over a broad range of transition metal concentrations. For BaTiO3, both Co and Mn implantation produced magnetic ordering temperatures near 300 K with coercivities less than or equal to70 Oe. The M-T plots showed either a near-linear decrease of magnetization with increasing temperature for Co and a non-Brillouin shaped curve for Mn. No secondary phases were detected by high-resolution X-ray diffraction. The same basic trends were observed for both SrTiO3 and KTaO3, with the exception that at high Mn concentrations (similar to5 at.%) the SrTiO3 was no longer ferromagnetic. Our results are consistent with recent reports of room temperature ferromagnetism in other perovskite systems (e.g. LaBaMnO3) and theoretical predictions for transition metal doping of BaTiO3 [Nakayama et al., Jap. J. Appl. Phys. 40 (2001) L1355]. (C) 2003 Elsevier Ltd. All rights reserved.