Cobalt and nickel spinet ferrites with CoFe2O4 and NiFe2O4 stoichiometries have been prepared by a sol-gel process based on a vacuum sublimation of a citrate precursor. Several samples of CoFe2O4 were obtained by varying the conditions of citrate precursor formation and further annealing. SEM images demonstrated the strong influence of synthesis parameters on the morphologies of secondary and primary particles. The formation of layered flake-like aggregates defining a macroporous system is assumed to improve the electrolyte-electrode contact in iron-containing samples. An enhanced electrochemical performance was achieved for samples annealed at high temperatures, especially for CoFe2O4 heated at 1000 degrees C for 24 h. Capacity values higher than 700 mAh g(-1) was recorded after 75 cycles. Fe-57 Mossbauer spectroscopy was used to clarify aspects of the mechanism of the electrochemical reaction. (C) 2007 Elsevier B.V. All rights reserved.