The corrosion performance of various Fe-Al alloys in 62 mol. %Li2CO3-38 mol.%K2CO3 at 650 degrees C has been studied using the weight loss technique. Alloys included FeAl with additions of 1, 3 and 5 at.% of either Ni or Li with or without a heat treatment at 400 degrees C during 144 h. For comparison, 316L type stainless steel was also studied. The tests were complemented by X-ray diffraction (XRD), scanning electronic microscopy and microchemical studies. Results showed that FeAl base alloy without heat treatment had the highest corrosion rate but by either heat treating it or by adding either Ni or Li the mass gain was decreased. When the FeAl base alloy was heat treated and alloyed with either 5Ni or 1Li the degradation rate reached as low values as those found for 316L stainless steel which had the lowest degradation rate. Both Ni and Li improved the adhesion of external protective layer either by avoiding the formation of voids or by lowering the number of precipitates and making them more homogenously distributed. (c) 2007 Elsevier B.V. All rights reserved.