SEM study of the morphologic change of high-density polyethylene surface grafted with glycidyl methacrylate
Scanning electron microscopy (SEM) study of the morphologic change of high-density polyethylene (HDPE) surface grafted with glycidyl methacrylate (GMA) was reported. Radiation-induced grafting of GMA onto HDPE was carried out in acetone and dichloromethane solution, respectively. The effects of irradiation dose, atmosphere, and swelling time on grafting were investigated. Generally, the extent of grafting increased with irradiation dose, but for the grafting carried out in acetone solution, the extent of grafting initially increased with irradiation dose and then remained almost constant. The extent of grafting was higher in acetone solution than in dichloromethane solution at the same irradiation dose. The extent of grafting in nitrogen was higher than that in air. The successful grafting of GMA onto HDPE was confirmed by weighing and FTIR analysis. SEM investigations showed that the morphologies of the PE samples grafted in acetone solution were quite different to those grafted in dichloromethane. The grafting of GMA carried out in acetone was mainly on HDPE surface and that carried out in dichloromethane was mainly in the bulk of HDPE. (c) 2007 Wiley Periodicals, Inc.