Smooth (Ra approximate to 0. 1 nm) and rough (Ra approximate to 20 nm) coatings of 1H, 1H,2H,2H-perfluorodecyltrimethoxysilane (FAS17) were prepared by controlling process conditions. The water contact angles for the smooth and rough coatings were similar (107 degrees and 110 degrees, respectively), but their sliding angles differed considerably (10 degrees and 27 degrees, respectively). The surface potential on the smooth coating, assessed using Kelvin force microscopy, showed a sharp distribution, but that on the rough coating ranged widely, implying large chemical heterogeneity including residual SiOH groups. The freezing temperature of a supercooled water droplet on the rough coating was higher than that on the smooth coating.