The powders of Li1+yGe2-x-yTixAly(PO4)(3) (X=0.1 divided by 0.3,y=0.07 divided by 0.21) have been synthesized by a solid phase reaction. The structure of the compounds was determined by X-ray diffraction patterns from the powder. The compounds belong to the rhombohedral symmetry (s. g. R (3) over barc) with six formula units in the lattice. The sintering of the Li1+yGe2-x-yTixAly(PO4)(3) ceramics was conducted at temperature T= 1363 K for I h in air. The ionic conductivity of the ceramics was investigated by impedance spectroscopy in the frequency range from 1 MHz to 1.2 GHz at temperatures from 300 K to 600 K. Two dispersions regions were found in ionic conductivity spectra for all the compounds. The dispersions are caused by the ion transport in grain boundaries and in grains of the ceramic samples. The substitution of Ge4+-> Ti4+, Al3+ leads to the changes in the structure parameters and electrical properties of the compounds. (C) 2007 Elsevier B.V. All rights reserved.