Scanning Kelvin Probe (SKP) measurements of thin amorphous conversion film coated galvanised steel in combination with current density-potential curves and electrochemical impedance spectroscopy (EIS) were performed with the aim to improve the understanding of electrode potentials at the coating/metal interface and their influence on corrosive de-adhesion. The thin hybrid conversion films contained Zn-phosphates, fitanates and also complexing organic compounds and led to an inhibition of the cathodic oxygen reduction and anodic zinc dissolution. In the polymer coated area the conversion film leads to a cathodic shift of the potential as measured by means of the SKP. This cathodic potential shift is explained by the substitution of the n-semiconducting Zn-oxide with an insulating inorganic layer. When the SKP detects the potential of freely corroding iron at a defect, where no protective coating layer is, the interfacial potential for the conversion film coated zinc layer is more negative than the defect potential. This leads to a diminished driving force for an oxygen reduction induced delamination process which is of relevance for the understanding of cut-edge corrosion. (c) 2007 Elsevier Ltd. All rights reserved.