Journal of Applied Polymer Science, Vol.107, No.4, 2531-2538, 2008
Effect of foaming temperature and rubber grades on properties of natural rubber foams
Foaming temperature and grade of dry natural rubber were varied to evaluate their effects on the morphology and mechanical properties of natural rubber (NR) foams. Three different grades of NR were used; namely ENR-25, SMR-L, and SMR-10. NR foams from these grades were produced at three different foaming temperatures, i.e. 140, 150, and 160 degrees C. The study was carried out using formulated compositions containing sodium bicarbonate as the chemical blowing agent and were expanded using conventional compression molding technique via a heat transfer foaming process. The NR foams were characterized with respect to their relative foam density, density of crosslinking, cell size, compression stress, and compression set. Increase in foaming temperature resulted in lower relative density and larger cell size. It was also discovered that the crosslink density slightly decrease with increasing foaming temperature. For mechanical properties, the highest foam density resulted in the highest compression stress. Compression stress at 50% strain increased with increasing foaming temperature and ENR-25 foam has the highest compression stress among the produced foams. The results showed that the morphology, physical, and mechanical properties of the rubber foams can be controlled closely by the foaming temperature and rubber grades. (c) 2007 Wiley Periodicals, Inc.