To improve their adhesion properties, ultra high modulus polyethylene (UHMPE) fibers were treated by an atmospheric pressure helium plasma jet (APPJ), which was operated at radio frequency (13.56 MHz). The surface properties of the fibers were investigated by X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), and contact angle measurement. The surface dyeability improvement after plasma treatments was investigated using laser scanning confocal microscopy (LSCM). The adhesion strengths of the fibers with epoxy were evaluated by microbond tests. In addition, the influence of operational parameters of the plasma treatment including power input and treatment temperature was studied. XPS analysis showed a significant increase in the surface oxygen content. LSCM results showed that the plasma treatments greatly increased fluorescence dye concentrations on the surface and higher diffusion rate to the fiber center. The tensile strength of UHMPE fiber either remained unchanged or decreased by 10-13.6% after plasma treatment. The contact angle exhibited a characteristic increase in wettability, due to the polar groups introduced by plasma treatment. The microbond test showed that the interfacial shear strengths (IFSS) increase significantly (57-139%) after plasma treatment for all groups and the optimum activation is obtained at 100 degrees C and 5 W power input. SEM analysis showed roughened surfaces after the plasma treatments. (C) 2007 Wiley Periodicals, Inc.