Two series of alumina-supported molybdenum phosphide (MoP) catalysts with low and high metal loadings were prepared by temperature-programmed reduction of the oxidic catalyst precursors in hydrogen to different temperatures (823, 923, 1023 and 1123 K, respectively). Effects of reduction temperature and metal loading on the surface distribution and the type of species formed were studied by TPR, S-BET, XRD, HRTEM, P-31 NMR, Al-27 NMR and in the reaction of dibenzothiophene (DBT) hydrodesulfurization (HDS) performed in a flow reactor at 553 K and total hydrogen pressure of 3.4 MPa. HRTEM and P-31 NMR confirmed formation of Mo phase on all catalysts. The 9.9 wt% Mo catalyst activated at lowest reduction temperature (823 K) was found to be most active among the catalysts studied. The presence of a low amount of Mo-0 species on the surface of this catalyst does not appear to be a drawback for the catalytic activity. The increase in both metal loading (from 9.9 to 15 wt% Mo and from 3.2 to 4.8 wt% P) and reduction temperature (from 823 to 1123 K) was found to be detrimental for HDS activity due to sintering of active phase, and also to decrease in specific area and formation of phosphate species. (c) 2007 Elsevier B.V. All rights reserved.