Poly(trimethylene terephthalate) (PTT)/poly (carbonate of bisphenol A) (PC) blends were obtained in the melt state by direct injection molding and also by extrusion followed by injection molding. The blends rich in PTT were monophasic, while the blends rich in PC were biphasic with the two components of the blends present in both phases. Both the monophasic and biphasic blends were partially miscibilized, and also partially reacted, as observed by FTIR. The extent of the reaction was greater in previously mixed blends. The observed synergism in the modulus of elasticity was attributed to the increased orientation of the blend components upon blending. Although decreases in elongation at break were observed and attributed to degradation of PTT, the blends were clearly ductile and compatible. This was a consequence of either their monophasic structure, or of the presence of the two components in the two phases of the blends. (C) 2008 Wiley Periodicals, Inc.