The unexpected SOFC hetero-epitaxial system with large lattice mismatch is demonstrated. A (110)-oriented flat epitaxial film of Nd2NiO4+delta is successfully grown on the (100) surface of yttrium-stabilized zirconia, which realizes selective exposure of the active surface for oxygen reduction. The charge-transfer process is analyzed to be the rate-limiting step with a simple impedance model.