The average measured Hv for polycrystalline ReB2 and Ti-B composites under different loads shows that the tendency of Hv to decrease becomes weak for large loads, and the measured hardness of ReB2 is always lower than that of Ti-B composites. For comparison, the results from Chung et al. were inserted into the figure.