Nickel/yttria-stabilized zirconia (Ni/YSZ) is the conventional anode material for solid oxide fuel cells (SOFC). Although these anodes have many advantages, they suffer from carbon formation when exposed to hydrocarbon feeds. One potential way to decrease the severity and extent of carbon formation is to increase the hydrogen content of the feed. In this work, Ni/YSZ composites have been prepared and exposed at 1073 K to humidified feeds containing hydrogen to methane ratios varying between 0 and 1.5. The Ni/YSZ composites were analyzed using temperature-programmed oxidation (TPO), temperature-programmed hydrogenation (TPH), and scanning electron microscopy (SEM). Our results demonstrated that TPH techniques can be effectively used to characterize and fully remove the carbon formed on Ni/YSZ composites provided that the hydrogen content of the analysis stream is sufficient. Hydrogen addition to methane in the inlet feed significantly decreased the degree of carbon formation, and removal of the carbon using hydrogen rather than oxygen resulted in less damage to the microstructure. (c) 2008 Elsevier B.V. All rights reserved.