In this paper we present results on the characterization of Zn-doped InGaAsSb epitaxial layers to be used in the development of stacked solar cells. Using the liquid phase epitaxy technique we have grown p-type InGaAsSb layers, using Zn as the dopant, and n-type Te-doped GaSb wafers as substrates. A series of Zn-doped InGaAsSb samples were prepared by changing the amount of Zn in the melt in the range: 0.1-0.9 mg to obtain different p-type doping levels, and consequently, different p-n region characteristics. Low temperature photoluminescence spectra (PL) were measured at 15 K using at various excitation powers in the range 80-160 mW. PL spectra show the presence of an exciton-related band emission around 0.642 eV and a band at 0.633 eV which we have related to radiative emission involving Zn-acceptors. Using the photoacoustic technique we measured the interface recombination velocities related to the interface crystalline quality, showing that the layer-substrate interface quality degrades as the Zn concentration in the layers increases. (c) 2008 Elsevier B.V. All rights reserved.