Applied Surface Science, Vol.255, No.10, 5405-5408, 2009
Time-resolved transmission study of fused silica during laser-induced backside dry etching
Laser-induced backside dry etching (LIBDE) is a promising technique for micro-and nanomachining of transparent materials. Although several experiments have already proved the suitability and effectiveness of the technique, there are several open questions concerning the etching mechanism and the concomitant processes. In this paper time-resolved light transmission investigations of etching process of fused silica are presented. 125 nm thick silver coating was irradiated through the carrying 1 mm thick fused silica plate by single pulses of a nanosecond KrF excimer laser. The applied fluences were 0.38, 0.71 and 1 J/cm(2). During the etching process the irradiated spots were illuminated by an electronically delayed nitrogen laser pumped dye laser. The delay between the pump and probe pulses was varied in the range of 0 ns and 20 mu s. It was found that the transmitted probe beam intensity strongly depends on the applied delays and fluences. Scanning electron microscopy and energy dispersive X-ray spectrometry of the etched surface showed the existence of silver droplets and fragments on the illuminated surfaces and silver atoms built into the treated surface layer influencing the transmission behavior of the studied samples. (C) 2008 Elsevier B. V. All rights reserved.