A method of surface alloying treatment has been developed: Ni powders were welded into the surface of iron plates by Surface Mechanical Attrition Treatment (SMAT), followed by annealing at certain temperature for 30 min. A Ni-Fe alloy layer with thickness about 100 mu m in the sample surface was fabricated on pure iron plate. Scanning electron microscope (SEM), glow discharge spectrum (GDS), and X-ray diffraction (XRD) methods were used to analyze the microstructure, the composition and the phases of the alloy layer. Studies on the interface microstructure indicated that there was significant atomic diffusion and formation of multilayer of intermetallic compound and solid solution in SMAT process. Subsequent annealing accelerates the alloying process. The corrosion test shows the sample by SMAT treated with Ni powders exhibit the best corrosion resistance. (C) 2009 Elsevier B. V. All rights reserved.