A new catalytic oxidation using 2,2,6,6-tetramethylpiperidinyl-1-oxyl (TEMPO) and NaClO is applied to hardwood cellulose in water at 60 degrees C and pH 6.8 with NaClO2 used as a primary oxidant. The oxidized celluloses with carboxylate content of approximately 0.8 mmol/g were convertible to highly crystalline and individual fibrils 5 nm in width and at least 2 mu m in length by disintegration in water. The oxidized celluloses had no aldehyde groups, and high degrees of polymerization of more than 900. Solid-state C-13 NMR and X-ray analyses revealed that the C6 carboxylate groups formed are selectively present on the crystalline fibril surfaces at high densities. Films prepared from the dispersions were transparent and flexible, and exhibited a high tensile strength of 312 MPa even at a low density of 1.47 g/cm(3).