The importance of flame-retardant and smoke-suppressed poly(vinyl chloride) (PVC) compositions is increasing gradually in the polymer industry since PVC releases smoke and toxic gases (hydrogen chloride, HCl) during heating at temperatures above 140 degrees C with the result of dehydrochlorination reaction. In this study, the synergistic effects of zinc borate (ZB)-zinc phosphate (ZP) on the thermal stability of PVC were investigated using thermal techniques. The induction and stability time values of PVC plastigels were obtained at 140 degrees and 160 degrees C. The results revealed that PVC plastigels having only ZP and ZB retarded dehydrochlorination of PVC compared with the unstabilized sample. However, the plastigels with both ZB and ZP had a superior synergistic effect on char formation of PVC. Since the induction periods of the samples having both ZB and ZP were higher than those of the unstabilized samples having only ZB or only ZP, the synergistic effect was observed.