Electric arc filter dust (EAF dust) is a waste by-product which occurs in the production of steel. Instead of being disposed of, it can be used in cement composites for civil engineering, and for balances in washing machines. To estimate the environmental impact of the use of EAF dust in cement composites leachability tests based on diffusion were performed using water and salt water as leaching agents. Compact and ground cement composites, and cement composites with addition of 1.5% of EAF dust by mass were studied. The concentrations of total Cr and Cr(VI) were determined in leachates over a time period of 175 days. At the end of the experiment the concentrations of some other metals were also determined in leachates. The results indicated that Cr in leachates was present almost solely in its hexavalent form. No leaching of Cr(VI) was observed in aqueous leachates from compact cement composites and compact cement composites to which different quantities of EAF dust have been added. In ground cement composites and in ground cement composites with addition of EAF dust, Cr(VI) was leached with water in very low concentrations up to 5 mu g L-1. Cr(VI) concentrations were higher in salt water leachates. In compact and ground cement composites with addition of EAF dust Cr(VI) concentrations were 40 and 100 mu g L-1, respectively. It was experimentally found that addition of EAF dust had almost no influence on leaching of Cr(VI) from cement composites. Leaching of Cr(VI) originated primarily from cement. Leaching of other metals from composites investigated did not represent an environmental burden. From the physico-mechanical and environmental aspects EAF dust can be used as a component in cement mixtures. (C) 2008 Elsevier B.V. All rights reserved.