Poly(ethylene terephthalate) (PET)/Barite nanocomposites were prepared by direct melt compounding. The effects of PET-Barite interfacial interaction on the dynamic mechanical properties and crystallization were investigated by DMA and DSC. The results showed that Barite can act as a nucleating agent and the nucleation activity can be increased when the Barite was surface-modified (SABarite). SABarite nanoparticles induced preferential lamellae orientation because of the strong interfacial interaction between PET chains and SABarite nanoparticles, which was not the case in Barite filled PET as determined by WAXD. For PET/Barite nanocomposites, the Avrami exponent n increased with increasing crystallization temperature. Although at the same crystallization temperature, the n value will decrease with increasing SABarite content, indicating of the enhancement of the nucleation activity. Avrami analyses suggest that the nucleation mechanism is different. The activation energy determined from Arrhenius equation reduced dramatically for PET/SABarite nanocomposite, confirming the strong interfacial interaction between PET chains and SABarite nanoparticles can reduce the crystallization free energy barrier for nucleus formation. In the DSC scan after isothermal crystallization process, double melting behavior was found. And the double endotherms could be attributed to the melting of recrystallized less perfect crystallites or the secondary lamellae produced during different crystallization processes. (C) 2009 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 47: 655-668, 2009