A novel macro/nano blended nonwoven with excellent physical properties was prepared by electrospinning polyurethane (PU) nanofibers onto the surface of ramie webs under different weight ratios of NN-dimethylacetamide (DMAc)/acetone cosolvents. The ratio of cosolvents has a significant influence on the morphology, tensile properties, resilience, and thermal properties of the resultant samples. Bead-free and fine interconnected nanofibers were obtained with an increase of acetone content up to 60 wt%. The total physical properties of the blended nonwovens were optimal for a DMAc/acetone ratio of 40/60, in which the tensile load at break, extension at break and Young's modulus were 441, 54, and 256% higher than that of pure ramie web, respectively. The resilience of the blended nonwovens was similar to 20% higher than that of nonblended ramie web. The significant improvement of physical properties may be due to the good connection between PU nanofiber membranes and ramie webs and the molecular chain structure differences, interconnected structural differences, and high extensibility of PU nanofibers, according to the results of crystallization by differential scanning calorimetry (DSC) and morphological observation by scanning electronic microscopy (SEM). (C) 2009 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 48: 1-14, 2010