Cathode materials Nd2-xSrxNiO4 were prepared by the glycine-nitrate process and characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), AC impendence spectroscopy and DC polarization method, respectively. The results show that 110 reaction occurred between the electrode and the CGO electrolyte at 1100 C and the electrode formed good contact with the electrolyte after being sintered at 1000 C for 4 h. The rate-limiting step for oxygen reduction reaction oil Nd1.6Sr0.4NiO4 electrode changed with oxygen partial pressure and measurement temperature. The Nd1.6Sr0.4NiO4 electrode gave a polarization resistance of 0.93 Omega cm(2) at 700 C in air, which indicates that Nd2-xSrxNiO4 electrode is a promising cathode material for intermediate-temperature solid oxide fuel cell (IT-SOFC). (C) 2008 Elsevier B.V. All rights reserved.